Product Data Sheet &
General Processing Conditions
PermaStat® 200 A
Nylon 6 (PA)
ESD Protection
Permanently Anti-static
PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS | |||||
PERMANENCE | English | SI Metric | ASTM TEST | ||
| Specific Gravity | 1.13 | 1.13 | D 792 | ||
| Molding Shrinkage | |||||
| 1/8 in (3.2 mm) section | 0.0100 - 0.0150 in/in | 1.00 - 1.50 % | D 955 | ||
MECHANICAL | |||||
| Impact Strength, Izod | |||||
| notched 1/8 in (3.2 mm) section | 3.0 ft-lbs/in | 160 J/m | D 256 | ||
| unnotched 1/8 in (3.2 mm) section | 20.0 ft-lbs/in | 1068 J/m | D 4812 | ||
| Tensile Strength | 8000 psi | 55 MPa | D 638 | ||
| Tensile Elongation | > 10.0 % | > 10.0 % | D 638 | ||
| Tensile Modulus | 0.35 x 10^6 psi | 2413 MPa | D 638 | ||
| Flexural Strength | 11000 psi | 76 MPa | D 790 | ||
| Flexural Modulus | 0.30 x 10^6 psi | 2068 MPa | D 790 | ||
ELECTRICAL | |||||
| Volume Resistivity | 1.0e9 - 9.9e10 ohm.cm | 1.0e9 - 9.9e10 ohm.cm | D 257 | ||
| Surface Resistivity | 1.0e10 - 9.9e11 ohm/sq | 1.0e10 - 9.9e11 ohm/sq | D 257 ESD STM11.11 | ||
| Surface Resistance | 1.0e9 - 9.9e10 ohm | 1.0e9 - 9.9e10 ohm | ESD STM11.11 | ||
| Static Decay | |||||
| MIL-PRF-81705D, 5kV to 50 V, 12% RH | < 2.00 s | < 2.00 s | FTMS101C 4046.1 | ||
| PROPERTY NOTES | |||||
| Data herein is typical and not to be construed as specifications. Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties. | |||||
GENERAL PROCESSING FOR INJECTION MOLDING | |||||
| English | SI Metric | ||||
| Injection Pressure | 10000 - 15000 psi | 69 - 103 MPa | |||
| Melt Temperature | 380 - 460 °F | 193 - 238 °C | |||
| Mold Temperature | 150 - 200 °F | 66 - 93 °C | |||
| Drying | 4 hrs @ 175 °F | 4 hrs @ 79 °C | |||
| Moisture Content | 0.20 % | 0.20 % | |||
| Dew Point | 0 °F | -18 °C | |||
PROCESSING NOTES | |||||
| Do not exceed 520 °F (270 °C) melt temperature. Desiccant Type Dryer Required. | |||||
16 Dec 2004 LCR
This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.
Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein. Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all molded articles will have the same properties as those listed.
No information supplied by RTP Company constitutes a warranty regarding product performance or use. Any information regarding performance or use is only offered as suggestion for investigation for use, based upon RTP Company or other customer experience. RTP Company makes no warranties, expressed or implied, concerning the suitability or fitness of any of its products for any particular purpose. It is the responsibility of the customer to determine that the product is safe, lawful and technically suitable for the intended use. The disclosure of information herein is not a license to operate under, or a recommendation to infringe any patents.